Perpendicularly magnetized ferromagnetic layers having an oxide interface allowing for improved control of oxidation

ABSTRACT

An improved magnetic tunnel junction with two oxide interfaces on each side of a ferromagnetic layer (FML) leads to higher PMA in the FML. The novel stack structure allows improved control during oxidation of the top oxide layer. This is achieved by the use of a FML with a multiplicity of ferromagnetic sub-layers deposited in alternating sequence with one or more non-magnetic layers. The use of non-magnetic layers each with a thickness of 0.5 to 10 Angstroms and with a high resputtering rate provides a smoother FML top surface, inhibits crystallization of the FML sub-layers, and reacts with oxygen to prevent detrimental oxidation of the adjoining ferromagnetic sub-layers. The FML can function as a free or reference layer in an MTJ. In an alternative embodiment, the non-magnetic material such as Mg, Al, Si, Ca, Sr, Ba, and B is embedded by co-deposition or doped in the FML layer.

RELATED PATENT APPLICATIONS

This application is related to the following: U.S. Pat. No. 8,592,927, filing date Nov. 23, 2015, Ser. No. 14/939,232, both assigned to a common assignee and herein incorporated by reference in their entirety.

TECHNICAL FIELD

The invention relates to a composite magnetic structure having a combination (stack) of oxide layers, ferromagnetic layers, and non-magnetic layers that improve the perpendicular magnetization used in magnetic thin films such that thermal stability is improved independent of the moment, volume, or crystalline anisotropy for a device with perpendicular magnetic anisotropy.

BACKGROUND

Magnetic thin films magnetized perpendicular to the plane of the film have many applications for memory and data storage technologies, e.g. magnetic hard disk drives, Magnetic Random Access Memories (MRAM) or magnetic domain wall devices.

Perpendicular magnetization relies on Perpendicular Magnetic Anisotropy (PMA), to overcome the magnetostatic shape anisotropy, the favored in-plane magnetization in thin film geometry.

Several physical phenomena can induce PMA, e.g. crystalline anisotropy, surface or interface anisotropy, and magnetoelastic anisotropy. Interfacial anisotropy occurs at an interface between an Oxide Layer (OL) (e.g. MgO) and a Ferromagnetic Layer (FML) (e.g. Fe, Co, CoFe or CoFeB), and is of particular technological importance. Indeed, this interface structure is widely used in MRAM devices, whose memory elements are based on magnetic tunnel junctions, each having two magnetic electrodes magnetized perpendicular to the plane of the Silicon wafer and separated by an oxide tunnel barrier.

In addition to the cited oxide and ferromagnetic layers, the magnetic tunnel junction (MTJ) structure can include a non-ferromagnetic metallic (ML), or seed layers, in a stacked structure. The simplest layered stack to create Perpendicular Magnetic Anisotropy (PMA) in one of the two magnetic electrodes of a Magnetic Tunnel Junction is to form a single ferromagnetic layer over a metallic layer, and then deposit an oxide layer over the ferromagnetic layer to give a stack designated from bottom to top ML/FML/OL, or in reverse order, OL/FML/ML.

Standard processes used in the semiconductor industry require heating wafers up to elevated temperatures as high at 400° C. for extended periods of time as long as several hours in an annealing process. Therefore MTJ devices constructed through semiconductor processes must withstand the temperature and time used in these standard processes without any degradation in magnetic and/or magneto-transport properties.

The Boltzmann Factor is the probability (p) in equation (1), that a thermal fluctuation causes a memory bit in an MTJ to flip between two stable states corresponding to a logical “0” and “1”. The thermal stability is related to the energy barrier between the two states (E), Boltzmann's constant (k_(B)), and the absolute temperature (T) in equation (2). Boltzmann Factor=p(E)=e ^(−Δ)  (1) Thermal Stability factor=Δ=E/k _(B) T  (2)

In the case of PMA, the energy barrier E depends on the magnetic anisotropy of the storage (i.e. free) layer. For a uniform magnetization reversal mechanism, the energy barrier E is proportional to the product of K_(eff)·t_(FML) where t_(FML) is the thickness of the ferromagnetic layer. K_(eff) is the effective anisotropy constant (having the dimension of an energy per unit volume).

K_(eff) can be modeled as the sum of the interfacial anisotropy and shape anisotropy. K _(eff)=Interfacial Anisotropy+Shape Anisotropy  (3)

Interfacial anisotropy is inherent in the material properties and is represented by a constant K_(i) (energy per unit surface) divided by the ferromagnetic layer film thickness. The shape anisotropy reduces the thermal stability and is modeled by equation (4), Shape Anisotropy=−2πM _(s) ²  (4)

where M_(s) is the saturation magnetization, and t_(FML) is the ferromagnetic layer film thickness. Interfacial Anisotropy causes PMA and the shape anisotropy reduces the PMA. In summary . . . . K _(eff) =K _(i) /t _(FML)−2πM _(s) ²  (5)

Therefore from equation 5 the thermal stability should improve as the ferromagnetic layer t_(FML) gets thinner. However, this model does not apply when t_(FML) gets below a critical thickness. Experimentation finds that below the critical thickness, the ferromagnetic layer loses its magnetization due to imperfections and inter-diffusion with neighboring non-magnetic elements. Therefore the thermal stability reaches its maximum at the critical ferromagnetic thickness in a simple ML/FML/OL stack.

The simple PMA stack only provides weak PMA since there is a single OL/FML interface. The interfacial anisotropy (K_(i)) is not strong enough to sustain PMA for ferromagnetic layers thicker than ˜15 Angstroms. Moreover, there is significant inter-diffusion between the ferromagnetic layer and the base metallic layer that is tantalum for example. Inter-diffusion can cause the interface between the ferromagnetic and metallic layers to be a magnetically “dead” layer. As a result, the magnetic properties of the ferromagnetic layer are found to degrade when t_(FML)<˜8 Angstroms. For this simple stack interface structure, the thermal stability at the critical ferromagnetic thickness is only ˜0.2 erg/cm² and too small for practical applications.

An improved interface structure can be created by two OL/FML interfaces, layered in the form OL/FML/OL. This leads to higher PMA and enables the use of a thicker ferromagnetic layer. However, it is difficult to fabricate using oxidation to form the second oxide layer without also oxidizing the ferromagnetic layer. This leads to thick magnetically dead layers, loss of magnetization, and an increase of the resistance—area product of the Magnetic Tunnel Junction (MTJ).

Thus, an improved MTJ is needed with two oxide/FML interfaces to provide high PMA in the reference and free layers. Furthermore, oxidation to form the upper (second) OL must be better controlled to prevent undesirable oxidation of the FML and loss of PMA.

SUMMARY

The objective of the present disclosure is to provide a stronger Magnetic Tunnel Junction by strengthening the characteristics of the Perpendicular Magnetic Anisotropy in the stack structure.

A second objective of the present disclosure is to provide a method of forming the MTJ of the first objective.

According to one embodiment, the MTJ has a FML formed between two oxide layers in a OL₁/FML/OL₂ scheme where FML has two sub-layers (FML₁, FML₂) in a FML₁/NML/FML₂ configuration where NML is a non-magnetic layer, and FML may be either a free layer or reference layer.

There are three ways the present disclosure improves the Magnetic Tunnel Junction and thermal stability over the prior art. First, the resputtering of the NML having a relatively high re-sputtering rate during the deposition of FML₂ leads to a smoother ferromagnetic layer. A similar concept was disclosed in related patent application Ser. No. 14/939,232 with regard to depositing a second seed layer with a low resputtering rate over a first seed layer having a high resputtering rate.

Secondly, the presence of an NML inhibits the crystallization of the FML₂. As a result, the FML₂ has smaller grains and thinner grain boundaries. This reduces the diffusion of oxygen from the top oxide layer OL₂ to the FML₂ layer below it.

Lastly, the NML is a more highly reactive material than the FML₁ and FML₂ sub-layers. Therefore it attracts oxygen that has diffused from the OL₂ into the FML₂.

Another embodiment contains a ferromagnetic layer comprised of three FML sub-layers and two NMLs in an alternating scheme (from bottom to top or vice versa) OL/FML₁/NML/FML₂/NML/FML₃/OL.

A third embodiment is a ferromagnetic layer comprised of a multiplicity of alternating “n+1” FML sub-layers and “n” NML layers. From bottom to top or vice versa, this stack is of the form OL/FML₁/NML₁/ . . . /FML_(n)/NML_(n)/FML_(n+1)/OL In a variation of the first, second, and third embodiments, the OL layers at the top or bottom of the stack may be replaced by an ML layer such as Tantalum, Tungsten, Molybdenum, Ruthenium, or Nickel-Chromium alloy. The ML/FML layer has an interfacial perpendicular magnetic anisotropy PMA.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a notional view of the prior art for a Magnetic Tunnel Junction having a bottom spin valve configuration that is utilized in an MRAM, spin transfer oscillator (STO), or read/write head.

FIG. 2 is an MTJ in a prior art top spin valve configuration with the reference layer above the tunnel barrier and functionally equivalent to FIG. 1.

FIG. 3a is cross-sectional view of a free layer formed between a tunnel barrier and an oxide capping layer in a MTJ with a bottom spin valve configuration wherein the free layer is a laminate comprised of a non-magnetic layer (NML) formed between two ferromagnetic layers (FMLs) according to an embodiment of the present disclosure.

FIG. 3b is a cross-sectional view of a reference layer (RL) formed between a seed layer and a tunnel barrier in a MTJ with a bottom spin valve configuration wherein the RL is a laminate comprised of a non-magnetic layer (NML) formed between two ferromagnetic sub-layers (FML₁ and FML₂) according to an embodiment of the present disclosure.

FIGS. 4a and 5a represent modifications of the FIG. 3a embodiment wherein the free layer has a plurality of “n” non-magnetic layers (NMLs) in the laminated stack of NMLs and “n+1” FML sub-layers.

FIGS. 4b and 5b represent modifications of the FIG. 3b embodiment wherein the reference layer has a plurality of “n” NMLs in the laminated stack of NMLs and “n+1” FML sub-layers.

FIG. 6 and FIG. 9 are cross-sectional views of a MTJ with a bottom spin valve and top spin valve configuration, respectively, wherein a free layer having a laminated stack of NMLs and FML sub-layers is formed between two oxide layers according to an embodiment of the present disclosure.

FIGS. 7-8 are cross-sectional views of a MTJ with a bottom spin valve and top spin valve configuration, respectively, wherein the free layer has a laminated stack of NMLs and FML sub-layers formed between an oxide layer and a non-magnetic layer according to an embodiment of the present disclosure.

FIG. 10 and FIG. 13 are cross-sectional views of a MTJ with a top spin valve and bottom spin valve configuration, respectively, wherein a reference layer having a laminated stack of NMLs and FML sub-layers is formed between two oxide layers according to an embodiment of the present disclosure.

FIGS. 11-12 are cross-sectional views of a MTJ with a top spin valve and bottom spin valve configuration, respectively, wherein the reference layer has a laminated stack of NMLs and FML sub-layers formed between an oxide layer and a non-magnetic layer according to an embodiment of the present disclosure.

FIGS. 14-15 are cross-sectional views of a MTJ with a bottom spin valve and top spin valve configuration, respectively, wherein the free layer is doped with a non-magnetic material.

FIGS. 16-17 are cross-sectional views of a MTJ with a top spin valve and bottom spin valve configuration, respectively, wherein the reference layer is doped with a non-magnetic material.

FIGS. 18-20 show a sequence of process steps during the fabrication of a MTJ with a free layer formed according to an embodiment of the present disclosure.

FIG. 21 shows a plot of the magnetization vs. magnetic field for various free layer thicknesses “t”, in Angstroms, of the prior art OL/FML/OL stack structure from FIG. 1.

FIG. 22 shows a plot of magnetization vs. magnetic field for various free layer thicknesses “t”, in Angstroms in a OL/FML₁(t₁)/NML/FML₂(t₂)/OL stack formed according to an embodiment of the present disclosure where t₁=t₂, and t=t₁+t₂.

FIG. 23 shows a plot of magnetization vs. magnetic field for various free layer thicknesses “t”, in Angstroms, in a OL/FML₁ (4 Angstroms)/NML₁/FML₂(t1)/NML₂/FML₃ (t₂)/OL stack formed according to another embodiment of the present disclosure where t₁/t₂=¾ and t=(4+t₁+t₂) Angstroms.

FIG. 24 shows a plot of the degraded magnetization vs. magnetic field for a free layer stack without an NML layer that has been annealed at 400° C. for five hours and illustrates that the range of FML thickness does not exhibit the square loop characteristic of PMA.

FIG. 25 shows a plot of the magnetization vs, magnetic field for a free layer stack with two NMLs that has been annealed at 400° C. for five hours.

DETAILED DESCRIPTION

The present disclosure is a MTJ wherein at least one of a free layer, reference layer, or dipole layer has perpendicular magnetic anisotropy that is maintained during 400° C. processing of the magnetic devices such as embedded MRAM and STT-MRAM, in spintronic devices such as microwave assisted magnetic recording (MAMR) and spin torque oscillators (STO), and in various spin valve designs including those found in read head sensors.

As disclosed in related U.S. Pat. No. 8,592,927, a MTJ may be comprised of a pinned layer, a tunnel barrier layer, and a magnetic element including a composite free layer having a magnetic saturation (M_(s)) reducing (moment diluting) layer formed between two magnetic sub-layers (FM₁ and FM₂). The FM, layer has a surface that forms a first interface with the tunnel barrier while the FM₂ layer has a surface facing away from the tunnel barrier that forms a second interface with a perpendicular Hk enhancing layer which is employed to increase the perpendicular anisotropy field within the FM₂ layer.

In related patent application Ser. No. 14/939,232, we disclosed an improved seed layer stack wherein a low resputtering rate layer with amorphous character such as CoFeB is deposited on a high resputtering rate layer that is Mg, for example, to provide a “smoothing effect” to reduce peak to peak roughness at a top surface of the uppermost NiCr seed layer in a Mg/CoFeB/NiCr configuration. Thus, the NiCr seed layer has a smooth top surface with a peak to peak thickness variation of about 0.5 nm over a range of 100 nm compared with a peak to peak variation of about 2 nm over a range of 100 nm in prior art seed layer films as determined by transmission electron microscope (TEM) measurements.

We have discovered that the MTJ structures disclosed in the aforementioned related applications may be further improved according to the embodiments described herein. The MTJ in the present disclosure is comprised of a stack structure with improved control of the oxidization of an oxide layer above the free layer or a reference layer. The free layer or reference layer consists of a multiplicity (n) of thin ferromagnetic layers (Fe, Co, CoFe, CoFeB or combination thereof) deposited in an alternating sequence with (n−1) NMLs having a high resputtering rate and low magnetic dilution effect. According to one embodiment, the MTJ has a FML formed between two oxide layers in a OL₁/FML/OL₂ scheme where FML has a FML₁/NML/FML₂ configuration. The role of the NMLs is threefold and thereby provides three advantages in performance compared with the prior art Magnetic Tunnel Junctions in FIG. 1 and FIG. 2.

First, the resputtering of the NML having a relatively high resputtering rate during the deposition of FML₂ in a FML₁/NML/FML₂ configuration leads to a smoother FML₂ ferromagnetic layer. In other embodiments, where a FML_(n) layer is deposited on a NML_(n−1) layer, a similar smoothing effect is realized for the top surface of the FML_(n) layer.

Secondly, the presence of an NML layer inhibits the crystallization of the FML₂ layer, or in more general terms, a NML_(n−1) layer inhibits crystallization in the overlying FML_(n) layer. As a result, the FML₂ layer (and FML_(n) layer) has smaller grains and thinner grain boundaries. This reduces the diffusion of oxygen from the top oxide layer OL₂ to the FML₂ layer below it.

Lastly, the NML is a more highly reactive material than the FML sub-layers. Therefore it attracts oxygen that has diffused from the OL₂ into the FML₂. As a result, the FML ferromagnetic sub-layers, and especially the upper FML_(n) sub-layer in a stack with “n” FML sub-layers and “n−1” NML layers, are less oxidized than in the prior art which leads to a better magnetoresistive ratio and greater FML thermal stability.

According to one embodiment of the present disclosure shown in FIG. 3a , the free layer 20-1 has a FML₁/NML₁/FML₂ configuration in which FML₁ 20 a made from Fe, Co, Ni, CoFe, CoB, FeB, CoFeB, CoFeNiB, or combination thereof, is deposited on the oxide tunnel barrier layer hereafter called the tunnel barrier 19. The tunnel barrier is a metal oxide or oxynitride comprised of one or more oxide or oxynitride layers made from one or more of Si, Ba, Ca, La, Mn, V, Al, Ti, Zn, Hf, Mg, Ta, B, Cu, Cr. NML₁ 20 b with a thickness from 0.5 to 10 Angstroms is then deposited over the first FML₁ 20 a. The NML₁ is a highly reactive metal with a relatively high re-sputtering rate and is typically a metal such as Mg, Al, B, Ca, Ba, Sr, Si, or C. Next a second FML₂ 20 c is deposited over the NML₁ 20 b and is selected from one of Fe, Co, Ni, CoFe, CoB, FeB, CoFeB, CoFeNiB, or a combination thereof.

The deposition of FML₂, which has a low resputtering rate compared with NML₁, resputters a portion of NML₁, which leads to a smoother top surface for both of NML₁ and FML₂. As described in related application Ser. No. 14/939,232, a high resputtering rate for material A vs. material B results from one or both of a higher bond energy and a higher atomic number for material B.

The presence of NML₁ prior to the deposition of FML₂ inhibits the crystallization of FML₂. As a result, FML₂ 20 c has smaller grains and thinner grain boundaries. This reduces the diffusion of oxygen from the subsequently deposited capping oxide layer 40 to the FML₂ layer below it. Furthermore, NML₁ 20 b is a more highly reactive material than the FML₂ layer. As a result, NML₁ 20 b attracts oxygen that has diffused from the top oxide layer 40 into the FML₂ and thereby prevents oxidation of the FML₂.

Referring to FIG. 3b , an alternative embodiment of the present disclosure is depicted wherein a reference layer 10-1 having a FML₁/NML₁/FML₂ configuration is formed between a seed layer 2 and tunnel barrier 19. The seed layer may be comprised of one or more metals or alloys such as those disclosed in related patent application Ser. No. 14/939,232, or other materials used in the art. The composition of the FML₁, NML₁, and FML₂ layers was described previously. In this case, the NML₁ layer serves to prevent oxidation of the FML₂ layer by attracting oxygen that diffuses into FML₂ from the tunnel barrier. Otherwise, all of the benefits associated previously described with forming a FML₁/NML₁/FML₂ stack apply to the reference layer 10-1.

According to another embodiment shown in FIG. 4a , the free layer laminated stack 20-1 described earlier is modified to form free layer 20-2 by sequentially depositing a NML₂ layer 20 d and FML₃ layer 20 e on the FML₂ layer to give a FML₁/NML₁/FML₂/NML₂/FML₃ configuration. NML₂ is selected from one of Mg, Al, B, Ca, Ba, Sr, Si or C, and FML₃ is made of one or more of Fe, Co, Ni, CoFe, CoFeB, CoB, FeB, and CoFeNiB. Capping layer 40 contacts a top surface of FML₃ 20 e. When the capping layer is an oxide, an oxide/FML₃ interface induces or enhances PMA in the FML₃ layer.

In FIG. 4b , the reference layer stack 10-2 in FIG. 3b may be enhanced to form an alternative embodiment where a FML₁/NML₁/FML₂/NML₂/FML₃ stack is formed between seed layer 2 and tunnel barrier 19. In other words, additional layers NML₂ and FML₃ are sequentially deposited on FML₂ to give a reference layer having the same advantages as reference layer stack 10-1. Again, the presence of an oxide tunnel barrier 19 adjoining a top surface of the upper FML layer induces or creates PMA in the upper FML (FML₃) layer.

In FIG. 5a , another embodiment of the present disclosure is depicted wherein the free layer laminated stack 20-1 described earlier is modified to form free layer stack 20-3 by depositing a plurality of “n−1” NML layers 20 b, 20 n−1, and “n” FML sub-layers 20 a, 20 c, 20 n in alternating fashion on the tunnel barrier 19 to give a FML₁/NML₁ . . . FML_(n−1)/NML_(n−1)/FML_(n) configuration. Each NML is selected from one of Mg, Al, B, Ca, Ba, Sr, Si, or C, and each FML sub-layer is made of one or more of Fe, Co, Ni, CoFe, CoFeB, CoB, FeB, and CoFeNiB. Capping layer 40 contacts a top surface of FML_(n) 20 n and may enhance PMA therein by forming an oxide layer/FML_(n) interface.

In FIG. 5b , the reference layer stack 10-1 in FIG. 3b may be enhanced to form an alternative embodiment to form reference layer stack 10-3 wherein a plurality of “n−1” NML layers and “n” FML sub-layers are deposited on seed layer 2 in alternating fashion to give a FML₁/NML₁ . . . FML_(n−1)/NML_(n−1)/FML_(n) configuration. Each NML is selected from one of Mg, Al, B, Ca, Ba, Sr, Si or C, and each FML sub-layer is made of one or more of Fe, Co, CoFe, CoB, FeB, CoFeB, and CoFeNiB. Tunnel barrier 19 contacts a top surface of FML_(n) 20 n and enhances or induces PMA therein by forming an oxide layer/FML_(n) interface. Thus, the process of depositing a FML sub-layer on a NML is repeated a plurality of times to reduce crystallization in each successive NML, provide a smoothing effect on a top surface of each FML sub-layer, and prevent oxidation of the FML_(n) by reacting with oxygen that may diffuse from the tunnel barrier into the FML_(n).

In all of the aforementioned embodiments, the present disclosure anticipates where one or more of the FML_(n) sub-layers may be comprised of a laminated stack such as (Co/X)_(m) or (X/Co)_(m) where m is from 1 to 30, and X is Pt, Pd, Ni, NiCo, Ni/Pt, or NiFe. In another aspect, CoFe or CoFeR may replace Co in the laminated stack where R is one of Mo, Mg, Ta, W, or Cr.

Referring to FIG. 6, the present disclosure also encompasses an embodiment wherein a MTJ encompasses a free layer stack 20-1, 20-2, or 20-3 formed between two oxide layers. In the exemplary embodiment, the free layer contacts a top surface of the tunnel barrier 19, and adjoins a bottom surface of an oxide capping layer 40 a. The oxide capping layer may be comprised of one or more oxide layers that are selected from the materials previously described with respect to tunnel barrier 19. In a bottom spin valve configuration, seed layer 2, reference layer 11, the tunnel barrier, the free layer, and capping layer 40 a are sequentially formed on a substrate 1 that may be a bottom electrode in a MRAM, a bottom shield in a read head sensor, or a main pole layer in a STO device. The reference layer may be a synthetic antiparallel (SyAP) configuration wherein an antiferromagnetic coupling layer such as Ru is formed between a lower AP2 ferromagnetic layer contacting the seed layer and an upper AP1 ferromagnetic layer (not shown) contacting the tunnel barrier. One or both of the AP2 and AP1 layers may be one or more of Co, Fe, Ni, CoB, FeB, CoFe, CoFeB, or CoFeNiB, or a laminate such as (Co/X)_(m) or (X/Co)_(m) described earlier. A top electrode 50 is formed on the capping layer and there may be an optional hard mask (not shown) such as MnPt between the capping layer and top electrode. In other embodiments, the top electrode is a top shield in a read head sensor or a trailing shield in a STO device.

Referring to FIG. 7, an alternative bottom spin valve MTJ is shown wherein all of the layers are retained from FIG. 6 except the oxide capping layer is replaced by a non-magnetic capping layer 40 b. In some embodiments, capping layer 40 b is one or more of Ru, W, Mo, NiCr, and Ta, including Ru/Ta and Ru/Ta/Ru configurations.

In FIG. 8, a MTJ with a top spin valve configuration is shown according to an embodiment of the present disclosure. All layers are retained from FIG. 7 except the positions of the free layer 20-1 (or 20-2 or 20-3) and reference layer 11 are switched so that the seed layer 2, free layer, tunnel barrier 19, reference layer, and capping layer 40 b are sequentially formed on substrate 1. The seed layer may be one or more of W, Ru, Ta, Mo, and NiCr.

In FIG. 9, another top spin valve configuration of the present disclosure is depicted that represents a modification of FIG. 6 where the free layer 20-1 (or 20-2 or 20-3), tunnel barrier 19, reference layer 11, and capping layer 40 b are sequentially formed on an oxide layer 15 above an optional seed layer 2 on substrate 1. Oxide layer 15 may be selected from one of the oxide materials previously mentioned with regard to oxide capping layer 40 a. As a result, there are two oxide layer/free layer interfaces at free layer top and bottom surfaces with tunnel barrier and oxide layer, respectively, to enhance PMA within the free layer.

Referring to FIG. 10, the present disclosure also anticipates the reference layer 10-1 (or 10-2 or 10-3) may be formed between two oxide layers in a top spin valve MTJ. In the exemplary embodiment, seed layer 2, free layer 21, tunnel barrier 19, the reference layer, and oxide capping layer 40 a are sequentially formed on substrate 1. Free layer 21 may be selected from the same materials as previously described with regard to reference layer 11. In this case, the reference layer has a first interface with the oxide tunnel barrier and a second interface with the oxide capping layer to enhance PMA in the reference layer.

In FIG. 11, another top spin valve MTJ is shown that retains all of the layers in FIG. 10 except the oxide cap layer is replaced with a non-magnetic capping layer 40 b described previously.

Referring to FIG. 12, a bottom spin valve MTJ is shown that retains all of the layers in FIG. 11. However, the positions of the free layer 21 and reference layer 10-1 (or 10-2 or 10-3) are switched such that the reference layer, tunnel barrier 19, free layer, and capping layer 40 b are sequentially formed on seed layer 2.

In FIG. 13, another bottom spin valve embodiment is illustrated that is a modification of the MTJ in FIG. 12 where seed layer 2 is replaced by an oxide layer 15 such that the reference layer has two oxide interfaces to enhance PMA therein.

According to another embodiment shown in FIG. 14, the non-magnetic material that attracts oxygen from a ferromagnetic layer (FML) may be embedded or doped within the FML 22 rather than forming a laminated stack of “n” FML sub-layers and “n−1” NMLs in earlier embodiments. Depending on the doped concentration in the FML, the non-magnetic material's efficiency in reacting with oxygen that may diffuse into the FML from an adjoining oxide layer may be less than in earlier embodiments involving the lamination of “n” FML sub-layers and “n−1” NMLs.

Moreover, the advantage of inhibiting crystallization in the FML may also be reduced compared with previous embodiments. Since a low resputtering rate material is not deposited on a high resputtering rate material in this embodiment, the smoothing effect of depositing a FML on a NML described earlier does not apply here.

Free layer 22 is doped or embedded with one or more of Mg, Al, Si, Ca, Sr, Ba, C, or B where the non-magnetic material has a concentration from 0.1 to 30 atomic % in the free layer. The non-magnetic material may be embedded in the free layer by a co-deposition process. The non-magnetic material has a magnetic dilution effect, which means that as the concentration of the non-magnetic element is increased in the free layer, the magnetic moment of the free layer is reduced. In the exemplary embodiment, an optional seed layer 2, reference layer 11, tunnel barrier 19, the free layer, capping layer 40 are sequentially formed on the substrate 1. Note that capping layer may comprise one or more non-magnetic metals as in 40 b or an oxide material as in 40 a.

In FIG. 15, the present disclosure also encompasses a top spin valve embodiment where oxide layer 15, free layer 22, tunnel barrier 19, reference layer 11, and capping layer 40 b are sequentially formed on substrate 1.

FIG. 16 represents a modification of the top spin valve MTJ in FIG. 15 wherein doped free layer 22 is replaced by free layer 21 described earlier while a reference layer 12 is employed that is doped with one or more of Mg, Al, Si, Ca, Sr, C, Ba or B. Thus, the MTJ stack has a seed layer/free layer/tunnel barrier/doped reference layer/capping layer configuration.

Referring to FIG. 17, a bottom spin valve MTJ is shown where oxide layer 15, doped reference layer 12, tunnel barrier 19, free layer 21, and cap layer 40 are sequentially formed on substrate 1.

The present disclosure also anticipates a method of forming a MTJ wherein a ferromagnetic layer comprises a laminated stack of FML sub-layers and NML layers as shown in FIGS. 3a-5b . In FIG. 18, an intermediate step is shown during the fabrication of MTJ 60 that is formed by sequentially forming a seed layer 2, reference layer 11, tunnel barrier 19, free layer 20-1 (or 20-2 or 20-3), and oxide capping layer 40 a on substrate 1. After all of the layers in the MTJ are formed by a conventional method, a photoresist layer 55 is coated and patterned on a top surface of the cap layer 40 a to form sidewall 55 s which is transferred through MTJ 60 by a subsequent ion beam etch (IBE) to form sidewall 60 s on the MTJ.

In FIG. 19, a dielectric layer 70 such as silicon oxide, silicon nitride or alumina is deposited to a level above the capping layer, and then a chemical mechanical polish (CMP) process is performed to remove the photoresist layer and form a top surface 70 t that is coplanar with a top surface 40 t of the capping layer 40 a.

Thereafter, in FIG. 20, the top electrode 50 is formed on the dielectric layer 70 and capping layer 40 a by a method well known to those skilled in the art.

FIGS. 21, 22, and 23 show the magnetic hysteresis loop for various stacks that have been annealed at 330° C. for thirty minutes using Kerr magnetometry. Magnetization is measured for fields between +1500 and −1500 Oe. Branches measured for increasing and decreasing fields are indicated as dashed and solid lines, respectively. The Kerr magnetization signal is proportional to the perpendicular magnetization. The thickness, t, is the total thickness of one or more FML. The figures of merit on these measurements are the squareness of the loops and the value of the coercive field.

The data shows the addition of one NML (FIG. 22) or two NML (FIG. 23) yields improved coercivity over a wider range in thicknesses. In particular, improved PMA is achieved down to layers thinner than 12 Angstroms. This is contrary to the prior art without NML shown in FIG. 21 for which the FML becomes discontinuous and loses its PMA below 12 Angstroms.

Another benefit is improved thermal budget in a magnetic tunnel junction having a free layer formed according to an embodiment described herein. FIGS. 24-25 show magnetic hysteresis loops for a stack without NML and one with two NMLs. Both stacks were annealed at 400° C. for 5 hours. The magnetic properties of the stack without NML are strongly degraded, as indicated by the reduction of squareness and coercive field. The magnetic signal is strongly reduced and vanishes for layers thinner than 14 Angstroms. Thicker layer do not exhibit square loops characteristic of perpendicular magnetization. By contrast, the stack having 2 NMLs retains square loops and non-zero coercive fields. This indicates that the stack retains good PMA after 5 hour annealing at 400° C. 

We claim:
 1. A magnetic structure comprising a ferromagnetic layer having perpendicular magnetic anisotropy (PMA) that is formed between a substrate and a first oxide layer (OL₁) wherein the ferromagnetic layer comprises: (a) a first ferromagnetic sub-layer (FML₁); (b) a first non-magnetic layer (NML₁) that is one of Sr, and Ba; and (c) a second ferromagnetic sub-layer (FML₂) to give a FML₁/NML₁/FML₂ configuration wherein the ferromagnetic layer (FML) contacts the OL₁ to generate PMA in the FML layer.
 2. The magnetic structure of claim 1 wherein the substrate is a second oxide layer (OL₂) that contacts a bottom surface of the FML₁ layer, and the first oxide layer contacts a top surface of the FML₂ layer to give an OL₂/FML₁/NML₁/FML₂/OL₁ configuration.
 3. The magnetic-structure of claim 2 wherein the first oxide layer is an Hk enhancing layer, the second oxide layer is a tunnel barrier layer, and the ferromagnetic layer is a free layer in a bottom spin valve configuration, or a reference layer in a top spin valve configuration.
 4. The magnetic structure of claim 2 wherein each of the first oxide layer and the second oxide layer is made of one or more of Si, Ba, Ca, La, Mn, V, Al, Ti, Zn, Hf, Mg, Ta, B, Cu, and Cr.
 5. The magnetic structure of claim 1 wherein each of the FML₁ and FML₂ sub-layers is selected from a group consisting of Fe, Co, Ni, CoFe, CoFeB, CoB, FeB, CoFeNiB, and combinations thereof.
 6. The magnetic structure of claim 1 wherein the first oxide layer is made of one or more of Si, Ba, Ca, La, Mn, V, Al, Ti, Zn, Hf, Mg, Ta, B, Cu, and Cr.
 7. The magnetic structure of claim 1 wherein each of FML₁ and FML₂ has a thickness from about 4 Angstroms to 14 Angstroms.
 8. The magnetic structure of claim 1 wherein the NML₁ layer has a thickness from about 3 Angstroms to 5 Angstroms.
 9. The magnetic structure of claim 1 wherein the ferromagnetic layer further comprises a second non-magnetic layer (NML₂) and a third ferromagnetic sub-layer (FML₃) to give a FML₁/NML₁/FML₂/NML₂/FML₃ configuration.
 10. The magnetic structure of claim 9 wherein the substrate is a second oxide layer (OL₂) that contacts a bottom surface of the FML₁ layer, and the first oxide layer enhances PMA in the FML₃ layer to give a OL₂/FML₁/NML₁/FML₂/NML₂/FML₃/OL₁ configuration.
 11. The magnetic structure of claim 9 wherein the ferromagnetic layer further comprises additional ferromagnetic sub-layers and non-magnetic layers for a total of “s” ferromagnetic sub-layers and “s−1” non-magnetic layers formed in alternating fashion to provide a FML₁/NML₁/FML₂/NML₂/FML₃/ . . . /NML_((s-1))/FML_(s) configuration where s≥4.
 12. A magnetic structure formed on a substrate and comprising a ferromagnetic layer that is a reference layer having perpendicular magnetic anisotropy (PMA) that is formed between a non-ferromagnetic metallic (NM) layer that is one of Mo, W, and NiCr, and a first oxide layer (OL₁) wherein the ferromagnetic layer comprises: (a) a first ferromagnetic sub-layer (FML₁); (b) a first non-magnetic layer (NML₁) that is one of Sr, and Ba; and (c) a second ferromagnetic sub-layer (FML₂) to give a FML₁/NML₁/FML₂ configuration wherein the ferromagnetic layer (FML) contacts the OL₁ to generate PMA in the FML layer.
 13. The magnetic structure of claim 12 wherein the OL₁ layer contacts a bottom surface of the FML₁ layer and the NM layer is a capping layer that contacts a top surface of the FML₂ layer to give an OL₁/FML₁/NML₁/FML₂/NM configuration.
 14. The magnetic structure of claim 12 wherein the first oxide layer (OL₁) is made of one or more of Si, Ba, Ca, La, Mn, V, Al, Ti, Zn, Hf, Mg, Ta, B, Cu, and Cr.
 15. A magnetic structure formed on a substrate and comprising a ferromagnetic (FM) layer that is a free layer having perpendicular magnetic anisotropy (PMA) wherein the FM layer has a first surface contacting a non-ferromagnetic metallic (NM) layer that is one or more of W, Mo, and NiCr, and a second surface that contacts a first oxide layer (OL₁), wherein the FM layer comprises: (a) a first ferromagnetic sub-layer (FML₁) formed on OL₁; (b) a first non-magnetic layer (NML₁) that is one of Sr, and Ba; and (c) a second ferromagnetic sub-layer (FML₂) to give a FML₁/NML₁/FML₂ configuration where FML₂ is an uppermost magnetic layer in the magnetic structure and contacts a bottom surface of the NM layer.
 16. The magnetic structure of claim 15 wherein each of FML₁ and FML₂ is selected from one of Fe, Co, Ni, CoFe, CoB, FeB, CoFeB, CoFeNiB, or a combination thereof, or is a laminated stack such as (Co/X)_(m) or (X/Co)_(m) where m is from 1 to 30, and X is Pt, Pd, Ni, NiCo, Ni/Pt, or NiFe.
 17. A magnetic structure comprising a ferromagnetic layer having perpendicular magnetic anisotropy (PMA) that is formed between a substrate and a first oxide layer (OL₁) wherein the ferromagnetic layer comprises: (a) a first ferromagnetic sub-layer (FML₁); (b) a first non-magnetic layer (NML₁) that is one of Sr, and Ba; and (c) a second ferromagnetic sub-layer (FML₂) where one or both of FML₁ and FML₂ have a (Co/X)_(m) or (X/Co)_(m) composition where m is a lamination number from 1 to 30, and X is Ni, NiCo, Ni/Pt, or NiFe to give a FML₁/NML₁/FML₂ configuration wherein the ferromagnetic layer (FML) contacts the OL₁ to generate PMA in the FML layer. 